异性钕铁硼PPS注塑粒料
| HCNYP80L | HCNYP90L | HCNYP100L | ||||
|
磁特性 Magnetic Properties |
剩磁 Residual Induction |
Br | mT | 600-630 | 620-680 | |
| kGs | 6.0-6.3 | 6.2-6.8 | ||||
|
磁感应矫顽力 Coercive Force |
Hcb | kA/m | 378-418 | 400-438 | ||
| kOe | 4.75-5.25 | 5.0-5.5 | ||||
|
内禀矫顽 Intrinsic Coercivity |
Hcj | kA/m | 955-1114 | 955-1114 | ||
| kOe | 12.0-14.0 | 12.0-14.0 | ||||
|
最大磁能积 Max.Product Energy |
（BH)max | kJ/cm3 | 59.7-67.7 | 67.7-75.6 | ||
| MGOe | 7.5-8.5 | 8.5-9.5 | ||||
|
物理特性 Physical Properties |
密度Density | ρ | g/cm3 | 4.5-4.9 | 4.6-4.9 | |
|
流动性 Melt Flow Rate |
MFR | g/10min | 300-500 | ≥200 | ||
| (330℃ 10kg） | ||||||
| 收缩率Shrinkage | % | 0.05-0.3 | 0.05-0.3 | |||
| 拉伸强度 Tensile Stength |
ASTM-D638 | MPa | ≥35 | ≥35 | ||
| 弯曲强度 Flexural Modulus |
ASTM-D790 | MPa | ≥75 | ≥75 | ||
| 弯曲弹性率 Flexural Modulus |
ASTM-D790 | Gpa | ≥15 | ≥15 | ||
| IZOD冲击强度 ZOD Impact Strength |
ASTM-D256 | (kJ/m2) | ≥6 | ≥6 | ||
| 射出成型条件 | ||||||
|
立式LT-35T (35ton ) Ring Φ10xΦ7x10 |
干燥条件Pre drying | ℃/hr | 120/4 | |||
|
料筒温度 Barrel Temp. |
T1（加料） | ℃ | 290 | 290 | ||
| T2 | ℃ | 310 | 310 | |||
| T3（料嘴） | ℃ | 330 | 330 | |||
|
模具温度 Mold Temp. |
℃ | 130 | 130 | |||
| 射出压力Pressure | MPa (kg/cm2） |
70.5 (719) |
70.5 (719) |
|||
| 设定速度Speed | % | 60 | 60 | |||
| 1、成型条件供客户参考，PPS料注射料筒温度最高不允许超过330度。（ Molding conditions for customers'reference, the highest temperature of PPS injection barrel is not allowed to exceed 330 degrees.） | ||||||
|
2、可按客户要求定制。（It can be customized according to customers'requirements） 北京钐元新材料股份有限公司 |
||||||